Publication:
The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes

Simple item page
dc.contributor.affiliationen_US
dc.contributor.authorNor Salwa Bt. Hamdanen_US
dc.date.accessioned2023-05-03T15:30:22Z
dc.date.available2023-05-03T15:30:22Z
dc.date.issued2001
dc.description.abstractThe measurement of the transport critical current of T1-1212 superconductor tapes at three different annealing temperature and time were completed and recorded using the 1uV/cm criteria. The superconductor tapes labeled asM1, M10 and M11 were annealed at temperature of 890C for 30 minutes, 800C for 30 minutes and 800C for 1 hour respectively. The readings for the V-1 characteristics were obtained through the implementation of the standard four-point probe attached to the superconductor tapes and immersed in the boiling temperature of liquid nitrogen. The values of the V-1 characteristics were converted to uV/cm values by dividing the voltage values with the length of two voltage probes. From 1uV/cm criteria for the three tapes, we found that M10 has the highest value of critical current, I and no critical current was obtained sample M1.en_US
dc.identifier.urihttps://irepository.uniten.edu.my/handle/123456789/20880
dc.language.isoenen_US
dc.subjectSuperconductivityen_US
dc.titleThe transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapesen_US
dc.typeResource Types::text::Thesisen_US
dspace.entity.typePublication