The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes

Loading...
Thumbnail Image
Date
2001
Authors
Nor Salwa Bt. Hamdan
Journal Title
Journal ISSN
Volume Title
Publisher
Research Projects
Organizational Units
Journal Issue
Abstract
The measurement of the transport critical current of T1-1212 superconductor tapes at three different annealing temperature and time were completed and recorded using the 1uV/cm criteria. The superconductor tapes labeled asM1, M10 and M11 were annealed at temperature of 890C for 30 minutes, 800C for 30 minutes and 800C for 1 hour respectively. The readings for the V-1 characteristics were obtained through the implementation of the standard four-point probe attached to the superconductor tapes and immersed in the boiling temperature of liquid nitrogen. The values of the V-1 characteristics were converted to uV/cm values by dividing the voltage values with the length of two voltage probes. From 1uV/cm criteria for the three tapes, we found that M10 has the highest value of critical current, I and no critical current was obtained sample M1.
Description
Keywords
Superconductivity
Citation