Effect of reflow soldering process on metallurgical bonding between Sn3.5Ag solder and ENIG substrates

No Thumbnail Available
Date
2011
Authors
Muhammad N.A.
Bais B.H.
Ahmad I.
Isnin A.
Journal Title
Journal ISSN
Volume Title
Publisher
Research Projects
Organizational Units
Journal Issue
Abstract
Reflow soldering process is one of the important steps in the manufacturing process for ball grid arrays. The purpose of this study is to observe the metallurgical bonding between Sn3.5Ag solder ball and electroless nickel immersion gold (ENIG) substrates after reflow soldering process. The reflow soldering process was performed at peak temperatures T peak of 246 and 251�C for 50 s by the rapid thermal processing system. Visual micrographs of these solder joints were performed in order to support the metallurgical bonding of Sn3.5Ag solder ball and ENIG substrate after the reflow soldering process. The formation of Ni 3Sn 4 intermetallic compounds (IMCs) at the Sn3.5Ag solder/Ni interface was dependent and continuous with one another compared to the initial IMC formation at Tpeak of ?246�C. It was also found that the initial IMCs thickness of Sn3.5Ag solder/Ni interface was lower and thinner at Tpeak of y251uC during the reflow soldering process. As a conclusion, the metallurgical bonding between Sn3?5Ag solder/ENIG substrate was formed better at T peak of ?251�C during the reflow soldering process using the rapid thermal processing system. � W. S. Maney & Son Ltd. 2011.
Description
Keywords
Elemental analysis , Intermetallic compounds , Metallurgical bonding , Reflow profile , Visual micrograph , Ball grid arrays , Chemical analysis , Flip chip devices , Intermetallics , Metallurgy , Rapid thermal annealing , Rapid thermal processing , Silver , Soldering alloys , Substrates , Tin , Electroless nickel immersion gold , Manufacturing process , Metallurgical bonding , Peak temperatures , Reflow profile , Reflow--soldering , Sn3.5Ag solder , Solder joints , Visual micrograph , Soldering