Publication: Alloyability of warm formed FeCrAl powder compacts
Date
2015
Authors
Rahman M.M.
Talib A.A.A.
Journal Title
Journal ISSN
Volume Title
Publisher
Elsevier Ltd
Abstract
Alloyability of warm formed Fe-based powder compacts is presented here. Iron (Fe) powder ASC100.29 was mixed with other alloying elements, namely chromium (Cr), and aluminum (Al) powder for 60. min and compacted at 150. �C by applying 130. kN axial loading, simultaneously from upper and lower punches to generate green compacts. The defect-free green compacts were subsequently sintered in argon gas fired furnace at 800. �C for three different holding times, i.e., 30, 60, and 90. min. Sintered samples were then analyzed through XRD and SEM/EDX for their alloyability. The results from XRD and SEM/EDX such as peak, intensity, microstructure, and element spectrum were studied. The flexure stress of the sintered samples was also measured to relate with their alloyability. The results revealed that the alloyability and microstructures of sintered products were affected by sintering time. The sample sintered for 60. min showed the highest intensity of FeCrAl alloy and bending strength. � 2015 Elsevier Ltd.
Description
Alloying elements; Aluminum alloys; Bending strength; Chromium alloys; Iron alloys; Microstructure; Sintering; Ternary alloys; X ray diffraction; Alloyability; Flexure stress; Green compacts; Powder compacts; Sintered products; Sintered samples; Sintering time; Warm powder compaction; Powders