Characterization of forming and sintering parameters in producing high quality components through warm compaction

Simple item page
dc.citedby0
dc.contributor.authorRahman M.M.en_US
dc.contributor.authorNor S.S.M.en_US
dc.contributor.authorRahman H.Y.en_US
dc.contributor.authorid55328831100en_US
dc.contributor.authorid23492827600en_US
dc.contributor.authorid7101793656en_US
dc.date.accessioned2023-12-29T07:47:23Z
dc.date.available2023-12-29T07:47:23Z
dc.date.issued2011
dc.description.abstractThis paper presents the outcomes of an experimental investigation on the effect of forming and sintering parameters to the quality of final products formed at above ambient temperature. The powder mass was prepared by mechanically mixing iron powder ASC 100.29 with 0.3 and 0.6 wt% of zinc stearate for 30 minutes. Solid cylindrical shape green samples were prepared by forming the powder mass at 30�C, 150�C, and 180�C by applying 100 kN axial load simultaneously from top and bottom punches. The defect-free samples were sintered in an argon gas fired sintering furnace by varying the sintering schedule. The as-formed green samples and the sintered products were characterized through density measurement, mechanical testing, and microstructure evaluation. The results revealed that high quality green samples could be produced by mixing 0.6 wt% zinc stearate with the main powder constituent and forming the powder mass at 180�C. The high quality finals products were obtained by sintering the green samples at 1000�C for 60 minutes at a heating/cooling rate of 10�C/minute.en_US
dc.description.natureFinalen_US
dc.identifier.epage242
dc.identifier.issue1
dc.identifier.scopus2-s2.0-84859779604
dc.identifier.spage234
dc.identifier.urihttps://www.scopus.com/inward/record.uri?eid=2-s2.0-84859779604&partnerID=40&md5=962afd6bcb61ca30cdf4d0c703d2ae65
dc.identifier.urihttps://irepository.uniten.edu.my/handle/123456789/30397
dc.identifier.volume7
dc.pagecount8
dc.sourceScopus
dc.sourcetitleMalaysian Journal of Microscopy
dc.subjectMechanical properties
dc.subjectMicrostructure
dc.subjectSintering schedule
dc.subjectWarm forming
dc.subjectZinc stearate
dc.titleCharacterization of forming and sintering parameters in producing high quality components through warm compactionen_US