Publication:
The effect of annealing to the hardness of high Y2O3-oxide dispersion strengthened (ODS) ferritic steels

Simple item page
dc.citedby4
dc.contributor.authorShamsudin F.M.en_US
dc.contributor.authorRadiman S.en_US
dc.contributor.authorAbdullah Y.en_US
dc.contributor.authorHamid N.A.en_US
dc.contributor.authorid57193534808en_US
dc.contributor.authorid6603411890en_US
dc.contributor.authorid6508386982en_US
dc.contributor.authorid6604077116en_US
dc.date.accessioned2023-05-29T06:57:07Z
dc.date.available2023-05-29T06:57:07Z
dc.date.issued2018
dc.descriptionalloy; annealing; compaction; dispersion; electron microscopy; hardness; oxide; steel; X-ray diffraction; yttriumen_US
dc.description.abstractThe purpose of this study was to investigate the effect of annealing to the hardness of high Y2O3-oxide dispersion strengthened (ODS) ferritic steels. The samples were prepared by mechanical alloying method followed by Cold Isostatic Pressing (CIP). After compaction process, the samples were sintered at 1100�C for 1 h in a tube furnace. The crystal structure and morphology of samples were analyzed by X-ray Diffraction (XRD) measurement and characterized by using field emission scanning electron microscope (FESEM), respectively. The hardness of samples was measured by using a micro-Vickers hardness tester with a load of 200 gf at annealing temperature of 600�C, 800�C and 1000�C, respectively. The Vickers hardness value (HV0,2) versus annealing temperature graph showed that the hardness of all samples started to decrease at temperature of 600�C due to grain growth. The hardness value of all samples (1Y and 5Y) identified at this annealing temperature is 855 HV0,2 and 808 HV0, 2, respectively.en_US
dc.description.natureFinalen_US
dc.identifier.doi10.17576/jsm-2018-4701-22
dc.identifier.epage193
dc.identifier.issue1
dc.identifier.scopus2-s2.0-85041891760
dc.identifier.spage189
dc.identifier.urihttps://www.scopus.com/inward/record.uri?eid=2-s2.0-85041891760&doi=10.17576%2fjsm-2018-4701-22&partnerID=40&md5=497c43c407b15db599cfba022ce6f8ca
dc.identifier.urihttps://irepository.uniten.edu.my/handle/123456789/24220
dc.identifier.volume47
dc.publisherPenerbit Universiti Kebangsaan Malaysiaen_US
dc.relation.ispartofAll Open Access, Bronze
dc.sourceScopus
dc.sourcetitleSains Malaysiana
dc.titleThe effect of annealing to the hardness of high Y2O3-oxide dispersion strengthened (ODS) ferritic steelsen_US
dc.typeArticleen_US
dspace.entity.typePublication
Files
Collections
SCOPUS