Publication: Pitting corrosion of triggering initial fractures of palm oil screw press machine shafts
No Thumbnail Available
Date
2010
Authors
Loganathan T.M.
Purbolaksono J.
Inayat-Hussain J.I.
Muthaiyah G.
Wahab N.
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
Investigation was carried out following the frequent occurrences of shaft failures in a number of palm oil screw press machines in a Malaysia palm oil mill company. Visual inspection, chemical analysis on the shaft material, fatigue analyses by utilizing traditional method and microscopic examinations were performed to support the investigation. Overview on pitting corrosion problems is presented. Common locations of the failure are at around bottom edges of keyway and shoulder fillets of the shafts. The findings indicate that pitting corrosion is identified as the main root causes of the premature shaft failures. In turn, poor surface condition would significantly reduce the fatigue endurance limit of the shafts under torsional loading. � 2010 Elsevier Ltd.
Description
Keywords
Failure analysis , Fatigue analysis , Pitting corrosion , Shaft , Visual inspection , Corrosion fatigue , Failure analysis , Induction motors , Inspection , Microscopic examination , Mining , Presses (machine tools) , Quality assurance , Vegetable oils , Visual communication , Fatigue analysis , Fatigue endurance limit , Malaysia , Palm oil , Pitting corrosion , Root cause , Screw press , Shaft , Shaft failure , Shaft material , Shoulder fillet , Surface conditions , Torsional loadings , Visual inspection , Pitting