Aspects of wear mechanisms of carbide tools when machine Hastelloy C-22HS

No Thumbnail Available
Date
2010
Authors
Kadirgama K.
Noor M.M.
Abou-El-Hossein K.A.
Mohammad B.
Habeeb H.H.
Journal Title
Journal ISSN
Volume Title
Publisher
Research Projects
Organizational Units
Journal Issue
Abstract
In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/TiN experienced severe intergranular fractures and cracks. High temperature causes the layer of the coating to wear off and subsequently the inserts damaged at fast rates. Both types of inserts suffered from high crater wear and thermal cracking. Most of the wear occurred at the nose and flank of the inserts. Generally, it was observed that carbide coated with TiALN/TiN cutting tool performed better than carbide coated TiCN/TiN cutting tool when milling Hastelloy C-22HS. � (2010) Trans Tech Publications.
Description
Keywords
Carbide inserts , Nickel superalloys , Tool wear , Carbide tools , Cracking (chemical) , Cutting tools , Hydraulic structures , Machine tools , Metal working tools , Nickel alloys , Scanning electron microscopy , Superalloys , Tribology , Wear of materials , Crater wear , Fast rate , Hastelloy , High temperature , Intergranular fracture , Microstructure defects , Nickel superalloy , SEM , Thermal cracking , Tool wear , Wear mechanisms , Carbides