Publication: Effects of sintering schedule on the characteristics of fe-based powder compacts formed through warm compaction route
dc.citedby | 3 | |
dc.contributor.author | Rahman M.M. | en_US |
dc.contributor.author | Rosli M.H. | en_US |
dc.contributor.author | Namasivayam D. | en_US |
dc.contributor.authorid | 55328831100 | en_US |
dc.contributor.authorid | 57193714646 | en_US |
dc.contributor.authorid | 57193703054 | en_US |
dc.date.accessioned | 2023-05-29T06:11:45Z | |
dc.date.available | 2023-05-29T06:11:45Z | |
dc.date.issued | 2016 | |
dc.description.abstract | This paper presents the sintering characteristics of Fe-based powder compacts formed through the warm compaction method. Iron powder ASC100.29 (73 wt%), chromium powder (22 wt%), and aluminium powder (5 wt%) were mixed mechanically for 60 mins in preparing the feedstock. The powder mixture was subsequently compacted at 200�C through simultaneous loading of 325 MPa from upper and lower punches. The defectfree green compacts were then sintered in an argon gas fired furnace at a rate of 10�C/min by varying the sintering time (30, 60, and 90 mins) and temperature (600, 750, and 900�C), respectively. The sintered samples were characterized through physical and mechanical properties and their microstructures were analysed through scanning electron microscopy. The results revealed that sintering at 900�C for 90 mins contributed to the highest volumetric expansion and relative density change, which are not expected in the powder metallurgy industries. A moderate sintering temperature of 750�C for a holding time of 60 mins was found to produce a sintered sample with higher bending strength. In these sintering conditions, better dispersion of the alloyed elements is also observed. � Universiti Malaysia Pahang Publishing. | en_US |
dc.description.nature | Final | en_US |
dc.identifier.doi | 10.15282/ijame.13.1.2016.4.0264 | |
dc.identifier.epage | 3177 | |
dc.identifier.issue | 1 | |
dc.identifier.scopus | 2-s2.0-85016055500 | |
dc.identifier.spage | 3168 | |
dc.identifier.uri | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85016055500&doi=10.15282%2fijame.13.1.2016.4.0264&partnerID=40&md5=206ba0d7ee54a2b7697f9d0d7b90f129 | |
dc.identifier.uri | https://irepository.uniten.edu.my/handle/123456789/22710 | |
dc.identifier.volume | 13 | |
dc.publisher | Universiti Malaysia Pahang | en_US |
dc.relation.ispartof | All Open Access, Gold | |
dc.source | Scopus | |
dc.sourcetitle | International Journal of Automotive and Mechanical Engineering | |
dc.title | Effects of sintering schedule on the characteristics of fe-based powder compacts formed through warm compaction route | en_US |
dc.type | Article | en_US |
dspace.entity.type | Publication |